The thermal processing quality of injection molding tooling has a great influence on the performance and service life of the mold. In real life and work, our mold workshop requires excellence in the design and production of various molds, and there will be problems in the specific operation. We will discuss and exchange the problems in the use of molds with the plastic injection mold company.


custom plastic injection tooling


The quenching deformation and cracking of custom plastic injection molds, and the early fracture in the use process are all related to the thermal processing technology of the mold.


(1) Forging process, which is an important link in the manufacturing process of mold working parts. For high-alloy tool steel molds, technical requirements are usually put forward for the metallographic structure of the material carbide distribution. In addition, the forging temperature range should be strictly controlled, the correct heating specification should be formulated, the correct forging force method should be adopted, and the slow cooling or timely annealing after forging should be used.


(2) Preliminary heat treatment. Depending on the material and requirements of the injection molding tooling, preliminary heat treatment processes such as annealing, normalizing or quenching and tempering are used to improve the structure, eliminate the structural defects of the forging blank, and improve the processing technology. High-carbon alloy die steel can eliminate network secondary cementite or chain carbide through proper preliminary heat treatment, spheroidize and refine the carbide, and promote the uniformity of carbide distribution. This will help ensure the quality of quenching and tempering and increase the life of the mold.


(3) Quenching and tempering. This is the key link in mold heat treatment. If overheating occurs during quenching and heating, it will not only cause greater brittleness of the workpiece, but also easily cause deformation and cracking during cooling, which will seriously affect the life of the mold. Special attention should be paid to prevent oxidation and decarburization during the quenching and heating of the die, and the heat treatment process specifications should be strictly controlled. When conditions permit, vacuum heat treatment can be used. After quenching, it should be tempered in time, and different tempering processes should be adopted according to the technical requirements.


(4) Stress relief annealing. The working parts of injection molding tooling should be subjected to stress relief annealing treatment after rough machining. The purpose is to eliminate the internal stress caused by rough machining, so as to avoid excessive deformation and cracks caused by quenching. For molds with high precision requirements, they need to undergo stress relief and tempering treatment after grinding or electrical machining, which is conducive to stabilizing the precision of the mold and improving the service life.


SERVICE

CONTACT

GoodTech MFG Group Limited
No. 22, Yuhua Road, Tangxia Town, Dongguan, 
Guangdong, China 523710  
Email: mark.li@goodtech-mfg.com

INQUIRY

GoodTech MFG Group Limited    All Rights Reserved     Technical Support:Molan Network